Er_2O_3对活性氧化铝热稳定性的影响  

The influence of Er2O3 on the hot stability of the active alumina

作　　者：刘晓军[1,2] 杨毅宏[1] 于海燕[1] 吴玉胜[1] 张林楠[3] 毕诗文[1] 

机构地区：[1]东北大学材料与冶金学院 [2]沈阳工业大学理学院,辽宁沈阳110023 [3]沈阳工业大学理学院

出　　处：《轻金属》2007年第7期15-17,共3页Light Metals

基　　金：国家自然科学基金(59974007);国家重点基础研究发展规划项目(GI9990664902)

摘　　要：本文系统研究了以Er2O3为添加剂时,Er2O3组分的添加对所得的γ-Al2O3热稳定性的影响。结果表明,Er2O3组分的适量添加可抑制高温下γ-Al2O3微孔的烧结和向α相的转变,从而提高氧化铝的热稳定性。本文采用X光衍射法测定α-Al2O3的含量。测得添加x(Er)=7%的样品在1200℃焙烧10h后.α-Al2O3转化率最低为35.86%。The thesis studies that the Er2O3 composing added influence the hot stability of the active alumina with the Er2O3 as additive, the result re-presses that the felicitousness of Er2O3 added restralnes the sinter of г-Al2O3 tiny bore and a phase transform trend towards α-Al2O3 at high tempera-ture, furthermore raising the hot stability of the alumina. This thesis uses the XRO method to measure the content of α-Al2O3. The α-Al2O3 content of the samples with x （Er） =7% sinter after 10 hours at 1200℃ is lowest 35.86%.

关 键 词：氧化铝 Er2O3 热稳定性 

分 类 号：O614.31[理学—无机化学]