磷酸修饰MCM-49分子筛的结构、酸性及苯与丙烯液相烷基化反应催化性能  

Structure and Acid Properties of Phosphate-modified MCM-49 Zeolites and Their Catalysis Performance for the Alkylation of Benzene with Propylene in Liquid

作　　者：张钰[1] 王丽霞[2] 吴淑杰[2] 杨胥微[2] 贾明君[2] 吴通好[2] 孙家锺[3] 

机构地区：[1]吉林化工学院化学工程系,吉林132022 [2]吉林大学化学学院物理化学系 [3]吉林大学理论化学计算国家重点实验室,长春130021

出　　处：《高等学校化学学报》2007年第9期1726-1730,共5页Chemical Journal of Chinese Universities

基　　金：国家自然科学基金(批准号:20273025);吉林省科委应用基础科技发展项目(批准号:20040572)资助.

摘　　要：在10L反应釜中用动态水热法合成了MCM-49分子筛,采用浸渍方法制备了磷酸修饰MCM-49分子筛,并用XRD,氮气吸附-脱附,NH3-TPD,FTIR和27AlMAS-NMR等方法进行了表征.考察了磷酸修饰MCM-49分子筛在苯与丙烯液相烷基化反应中的催化性能.NH3-TPD和FTIR表征结果说明,磷酸修饰处理使MCM-49分子筛的Brnsted酸和Lewis酸的酸量降低,强酸中心酸量略有降低.27AlMAS-NMR结果表明磷酸修饰使MCM-49分子筛骨架部分脱铝,脱除的铝与磷酸作用生成了磷铝酸盐.在实验条件下,MCM-49分子筛的丙烯转化率为99.6%,异丙苯选择性为75.3%.磷酸修饰处理提高了苯与丙烯液相烷基化反应产物中异丙苯的选择性.磷负载质量分数为2.0%的MCM-49的丙烯转化率和烷基化产物的总选择性(包括异丙苯、二异丙苯和三异丙苯)与MCM-49相当,而异丙苯的选择性提高了7.2%.MCM-49 zeolite was synthesized hydrothermally in a 10 L autoclave by dynamic method. The phosphate-modified MCM-49 zeolites were prepared by impregnation. The resulting solids were characterized by different techniques, such as XRD, N2 adsorption-desorption, NH3-TPD, FFIR and ^27Al NMR. Benzene alkylation with propylene was carried out by using MCM-49 and phosphate-loaded MCM-49 zeolite as the catalysts. Both the amounts of Bronsted and Lewis acid on phosphate-modified MCM-49 were decreased. ^27A1 NMR spectrum reveals that the loading of phosphate onto MCM-49 results in a increase of the amounts of extraframework aluminum, and two new signals corresponding to Al （OP）6 and Al （PO）4 can be found, respectively. Loading of phosphate onto MCM-49 greatly enhances the selectivity to IPB in benzene alkylation with propylene. The phosphate-modified MCM-49 catalyst containing 2.0% （mass fraction） phosphorus, at a reaction temperature of 140 ℃, exhibits 81.1% selectivity to IPB and 97.2% selectivity to all alkyahion products（ including IPB, DIPBs and TIPB） with a similar conversion of propylene in comparision with MCM-49.

关 键 词：MCM-49分子筛 苯和丙烯烷基化 磷酸 

分 类 号：O643.1[理学—物理化学]