COORDINATION CROSSLINKING OF NITRILE RUBBER FILLED WITH COPPER SULFATE PARTICLES  

作　　者：吴驰飞 

机构地区：[1]Polymer Alloy Laboratory School of Materials Science and Engineering,East China University of Science and Technology

出　　处：《Chinese Journal of Polymer Science》2007年第5期447-459,共13页高分子科学（英文版）

基　　金：This work was financially supported by the Program of National Natural Science Foundation of China(No.50473031).

摘　　要：By incorporating copper sulfate （CuSO4） particles into acrylonitrile butadiene rubber （NBR） followed by heat pressing, a novel vulcanization method is developed in rubber through the formation of coordination crosslinking. This method totally differs from traditional covalent or non-covalent vulcanization approaches of rubber. No other vulcanizing agent or additional additive is involved in this process. By analyzing the results of DMA, XPS and FT-IR, it is found that the crosslinking of CuSO4 particles filled NBR was induced by in situ coordination between nitrogen atoms of nitrile groups （-CN） and copper ions （Cu^2＋） from CuSO4. SEM and EDX results revealed the generation of a core （CuSO4 solid particle）- shell （adherent NBR） structure, which leads to a result that the crosslinked rubber has excellent mechanical properties. Moreover, poly（vinyl chloride） （PVC） and liquid acrylonitrile-butadiene rubber （LNBR） were used as mobilizer to improve the coordination crosslinking of CuSO4/NBR. The addition of PVC or LNBR could lead to higher crosslink density and better mechanical properties of coordination vulcanization. In addition, crystal water in CuSO4 played a positive role to coordination crosslinking of rubber because it decreased the metal point of CuSO4 and promoted the metal ionization.By incorporating copper sulfate （CuSO4） particles into acrylonitrile butadiene rubber （NBR） followed by heat pressing, a novel vulcanization method is developed in rubber through the formation of coordination crosslinking. This method totally differs from traditional covalent or non-covalent vulcanization approaches of rubber. No other vulcanizing agent or additional additive is involved in this process. By analyzing the results of DMA, XPS and FT-IR, it is found that the crosslinking of CuSO4 particles filled NBR was induced by in situ coordination between nitrogen atoms of nitrile groups （-CN） and copper ions （Cu^2＋） from CuSO4. SEM and EDX results revealed the generation of a core （CuSO4 solid particle）- shell （adherent NBR） structure, which leads to a result that the crosslinked rubber has excellent mechanical properties. Moreover, poly（vinyl chloride） （PVC） and liquid acrylonitrile-butadiene rubber （LNBR） were used as mobilizer to improve the coordination crosslinking of CuSO4/NBR. The addition of PVC or LNBR could lead to higher crosslink density and better mechanical properties of coordination vulcanization. In addition, crystal water in CuSO4 played a positive role to coordination crosslinking of rubber because it decreased the metal point of CuSO4 and promoted the metal ionization.

关 键 词：COORDINATION Crosslink network Copper ions Nitrile rubber Vulcanization. 

分 类 号：TQ330.1[化学工程—橡胶工业]