单分散性纳米Co_3O_4的制备及电化学性能研究  

Study on preparation and electrochemical performance of mono-dispersed nanosized Co_3O_4

作　　者：黄可龙[1] 刘人生[1] 杨幼平[1] 刘素琴[1] 龚本利[1] 

机构地区：[1]中南大学化学化工学院,湖南长沙410083

出　　处：《电源技术》2007年第9期680-682,共3页Chinese Journal of Power Sources

基　　金：中南大学"大学生创新创业启航行动"项目(ZE097)

摘　　要：以Co(NO3)2为钴源,NH3·H2O-NH4Cl为沉淀剂,H2O2为氧化剂,水和正丁醇作溶剂,聚乙二醇作分散剂,采用水热法制备了约15nm的单分散性类球形Co3O4。采用X射线衍射(XRD),透射电子显微镜(TEM)等手段对产物进行了表征;并对其电化学性能进行了测试,结果表明,采用水热法制备的单分散性纳米Co3O4的电化学性能优良;20次循环后比容量保持有555mAh/g。Mono-dispersed spherical Co3O4 with the particle size of 15 nm was synthesized successfully by hydrothermal method using Co（NO3）2.6 H2O as cobalt salt, NH3·H2O-NH4CI as precipitator, H2O2 as oxidant, water and n-butanol as solvent, polyethylene glycol as dispersant. The product was characterized by X-ray diffraction （XRD） and transmission electron microscopy （TEM）. The electrochemical performances of the samples synthesized by hydrothermal method were also investigated. They demonstrated high lithium storage capacity and good cyclability. After 20 cycles, the discharge capacity of nano-Co3O, retained 555 mAh/g.

关 键 词：单分散性 纳米颗粒 四氧化三钴 负极材料 

分 类 号：TM912.9[电气工程—电力电子与电力传动]