Mechanical characterization of the role of defects in sintered FeCrAIY foams  

作　　者：M.Kepets A.P.Dowling 

机构地区：[1]Engineering Department,Cambridge University,Cambridge CB2 1PZ,UK

出　　处：《Acta Mechanica Sinica》2007年第4期383-398,共16页力学学报（英文版）

基　　金：The project supported by the US 0ffice of Naval Research （N000140210117）; the National Basic Research Program of China （2006CB601202）; the National Natural Science Foundation of China （10328203, 10572111, 10632060）; the National 111 Project of China.（B06024）.

摘　　要：Open celled metal foams fabricated through metal sintering are a new class of material that offers novel mechanical and acoustic properties. Previously, polymer foams have been widely used as a means of absorbing acoustic energy. However, the structural applications of these foams are limited. The metal sintering approach offers a costeffective means for the mass-production of open-cell foams from a range of materials, including high-temperature steel alloys. In this first part of two-paper series, the mechanical properties of open-celled steel alloy （FeCrA1Y） foams were characterized under uniaxial compression and shear loading. Compared to predictions from established models, a significant knockdown in material properties was observed. This knockdown was attributed to the presence of defects throu- ghout the microstructure that result from the unique fabrication process. Further in situ tests were carried out in a SEM （scanning electronic microscope） in order to investigate the effects of defects on the properties of the foams. Typically, the onset of plastic yielding was observed to occur at defect locations within the microstructure. At lower relative densities, ligament bending dominates, with the deformation initializing at defects. At higher relative densities, an additional deformation mechanism associated with membrane elements was observed. In the follow-up of this paper, a finite element model will be constructed to quantify the effects of defects on the mechanical performance of the opencell foam.Open celled metal foams fabricated through metal sintering are a new class of material that offers novel mechanical and acoustic properties. Previously, polymer foams have been widely used as a means of absorbing acoustic energy. However, the structural applications of these foams are limited. The metal sintering approach offers a costeffective means for the mass-production of open-cell foams from a range of materials, including high-temperature steel alloys. In this first part of two-paper series, the mechanical properties of open-celled steel alloy （FeCrA1Y） foams were characterized under uniaxial compression and shear loading. Compared to predictions from established models, a significant knockdown in material properties was observed. This knockdown was attributed to the presence of defects throu- ghout the microstructure that result from the unique fabrication process. Further in situ tests were carried out in a SEM （scanning electronic microscope） in order to investigate the effects of defects on the properties of the foams. Typically, the onset of plastic yielding was observed to occur at defect locations within the microstructure. At lower relative densities, ligament bending dominates, with the deformation initializing at defects. At higher relative densities, an additional deformation mechanism associated with membrane elements was observed. In the follow-up of this paper, a finite element model will be constructed to quantify the effects of defects on the mechanical performance of the opencell foam.

关 键 词：Metal foam DEFECT Mechanical characterization SEM 

分 类 号：O186.1[理学—数学]