木材液化及其在聚氨酯胶黏剂上的应用研究  

Research of Liquefaction of Wood and Its Utilization for Polyurethane Adhesives

作　　者：张玉苍[1] 迟青山[1] 孙岩峰[1] 谭凤芝[1] 吴雄伟[1] 张文明[1] 

机构地区：[1]大连轻工业学院化工与材料学院,辽宁大连116034

出　　处：《林产化学与工业》2007年第5期73-77,共5页Chemistry and Industry of Forest Products

基　　金：大连市科技计划项目资助(2005E21SF146);辽宁省教育厅科技计划项目资助(05L065)

摘　　要：通过考察木粉在催化剂存在下的加溶剂液化,确定了木粉液化的最佳工艺条件,即:温度160℃,m(苯酚)∶m(木粉)为5∶1,催化剂用量1.2 mmol/g,反应时间60 min,残渣率降至3.5%。并发现随着反应时间的延长,液化物出现再凝聚的残渣。利用液化产物制备了聚氨酯胶黏剂,拉伸剪切强度达5 MPa,达到应用要求,为今后的工业化生产提供了依据。The optimum technical conditions of wood liquefaction are studied using waste wood powder with phenol as catalyst at 160 ℃, re（phenol） ： m（ wood powder） 5： 1, catalyst dosage 1.2 mmol/g, reaction time 6 rain, the residue rate can belowered to 3.5 %, New residue is originated from liaquefied product under prolonged reaction time. Polyurethane adhesives prepared from liquefied wood has the tensile strength of 5 MPa, which meets the application requirement. This study provides basis for its industrial production.

关 键 词：木材 液化 再凝聚的残渣 聚氨酯 拉伸剪切强度 

分 类 号：TQ433.432[化学工程]