表面掺杂CeO_2对2Y-TZP陶瓷抗低温水热腐蚀的影响  

Effects of Surface CeO 2 -doping on the Hydrothermal Corrosion Resistance of 2Y-TZP Ceramics at Low Temperature

作　　者：赵振波[1,2,3] 刘澄[1,2,3] 于晓东[1,2,3] 倪国年 

机构地区：[1]清华大学 [2]哈尔滨工业大学 [3]北京理工大学

出　　处：《稀有金属材料与工程》1997年第3期50-52,共3页Rare Metal Materials and Engineering

摘　　要：比较了对２Ｙ－ＴＺＰ陶瓷采用表面掺杂ＣｅＯ２和体掺杂ＣｅＯ２两种不同方式处理后，２Ｙ－ＴＺＰ陶瓷低温水热腐蚀前后的抗弯强度的变化。结果表明，对Ｙ－ＴＺＰ陶瓷进行表面掺杂ＣｅＯ２，不仅可以克服体掺杂ＣｅＯ２时抗弯强度大幅度下降的问题，而且可以明显改善低温水热腐蚀对Ｙ－ＴＺＰ陶瓷力学性能的影响。表面掺杂ＣｅＯ２对２Ｙ－ＴＺＰ陶瓷抗低温水热腐蚀的原因，是既保持了Ｙ－ＴＺＰ陶瓷整体对等温相变的约束，又阻止了Ｙ－ＴＺＰ陶瓷产生氧空位的综合作用。The bending strengths of 2Y-TZP treated by different methods are compared under the condition of low temperature hydrothermal corrosion The results show that the surface Ce-doping of Y-TZP ceramics may not only prevent the decrease of bending strength, but also can significantly improve its mechanical properties of in the presence of low temperature hydrothermal corrosion It has been shown that the effects of surface Ce-doping on the mechanical properties of 2Y-TZP ceramics after hydrothermal corrosion should be attributed to the combined effects of the retained high stress field and introduction oxygen vacancies into the structure

关 键 词：二氧化铈 2Y-TZP陶瓷 表面掺杂 水热腐蚀 

分 类 号：TG178[金属学及工艺—金属表面处理] TG174.41[金属学及工艺—金属学]