钨铜功能梯度材料中掺杂TiC和La_2O_3性能比较研究  

Comparative study on W/Cu FGMs doping TiC and La_2O_3

作　　者：张珂[1] 沈卫平[1] 葛昌纯[1] 

机构地区：[1]北京科技大学材料学院核聚变材料研究中心,北京100083

出　　处：《粉末冶金技术》2007年第5期352-354,359,共4页Powder Metallurgy Technology

摘　　要：采用超高压力通电烧结工艺制备了添加1%TiC和1%La2O3的W/Cu功能梯度材料(FGMs),分析研究了其烧结性能、层间剪切强度及抗热冲击性能。此功能梯度材料孔隙度在6%左右;梯度层间剪切强度从富W侧向富Cu侧逐步增高;在激光功率密度200MW/m2下,对此材料进行激光热冲击试验,冲击1 000次,含1%La2O3钨-铜梯度材料表面没有损坏,而含1%TiC钨-铜梯度材料表面出现裂纹。　W/Cu functionally graded materials（FGMs） doping 1%La2O3 and 1%TiC respectively were prepared by a way of graded sintering under ultra-high pressure（GSUHP）.Their performance of sintering,shearing strength between layers and thermal-shock resistance were studied.The specimens have low porosity（about 6%） and good performance in thermal-shock resistance. The shearing strength increases from tungsten to copper.With laser power density of 200 MW/m^2,thermal-shock resistance of specimens was tested（1 000 times）.Results show that there is no damage on the surface of material doping 1% La2O3,but cracks arise on the surface of material doping 1% TiC.

关 键 词：W/Cu FGMS TIC LA2O3 层间剪切强度 抗热冲击性能 

分 类 号：TB331[一般工业技术—材料科学与工程]