Aging behavior of Al_2O_3 short fiber reinforced Al-Cu alloy composites  

作　　者：耿林 许虹宇 余快 王洪林 

机构地区：[1]School of Materials Science and Engineering,Harbin Institute of Technology

出　　处：《中国有色金属学会会刊：英文版》2007年第5期1018-1021,共4页Transactions of Nonferrous Metals Society of China

基　　金：Project(2006CB605203-3) supported by the National Basic Research Program of China

摘　　要：Al2O3 short fiber reinforced Al-Cu composites containing 1%, 3%, 5% and 7% Cu were fabricated by a squeeze casting technique. The as-cast Al2O3/Al-Cu composites were solution treated at 535 ℃ and then aged at 170, 190 and 210 ℃, respectively. Age hardening behavior of the Al2O3/Al-Cu composites was analyzed by measuring the hardness of the samples at different aging temperatures and aging time. Microstructures of the composites were observed by transmission electron microscope(TEM). The results indicate that the hardness of the Al2O3/Al-Cu composites containing 7% Cu is much higher than that containing 1%-5% Cu because of the large amount of CuAl2 precipitant in the Al2O3/Al-Cu composite. With the increase of Cu content from 1% to 7%, the time needed for the appearance of peak hardness shortened, indicating that the addition of Cu can accelerate the kinetic of CuAl2 precipitation in the Al2O3/Al-Cu composites. The Al2O3/Al-Cu composite containing 7% Cu shows the highest increment of hardness by aging treatment. Therefore, in order to get a higher peak hardness, the Al2O3/Al-Cu composites need more Cu addition as compared with the un-reinforced Al-Cu alloys.Al2O3 short fiber reinforced AI-Cu composites containing 1%, 3%, 5% and 7% Cu were fabricated by a squeeze casting technique. The as-cast Al2O3/Al-Cu composites were solution treated at 535 ℃ and then aged at 170, 190 and 210 ℃, respectively. Age hardening behavior of the Al2O3/Al-Cu composites was analyzed by measuring the hardness of the samples at different aging temperatures and aging time. Microstructures of the composites were observed by transmission electron microscope（TEM）. The results indicate that the hardness of the Al2O3/Al-Cu composites containing 7% Cu is much higher than that containing 1%-5% Cu because of the large amount of CuAl2 precipitant in the Al2O3/Al-Cu composite. With the increase of Cu content from 1% to 7%, the time needed for the appearance of peak hardness shortened, indicating that the addition of Cu can accelerate the kinetic of CuAl2 precipitation in the Al2O3/Al-Cu composites. The Al2O3/Al-Cu composite containing 7% Cu shows the highest increment of hardness by aging treatment. Therefore, in order to get a higher peak hardness, the Al2O3/Al-Cu composites need more Cu addition as compared with the un-reinforced Al-Cu alloys.

关 键 词：Al-Cu复合物 AL2O3短纤维 合金 老化现象 

分 类 号：TG156.92[金属学及工艺—热处理]