09CuPTiRE钢连铸板坯表面纵裂分析和改进工艺实践  

Analysis and Improved Process Practice on Surface Longitudinal Crack of Concasting Slab of Steel 09CuPTiRE

作　　者：辛建卿[1] 余伟[2] 

机构地区：[1]太原钢铁(集团)有限公司技术中心,太原030003 [2]北京科技大学高效轧制国家工程研究中心,北京100083

出　　处：《特殊钢》2007年第6期59-60,共2页Special Steel

摘　　要：09CuPTiRE耐候钢(%:≤0.12C、0.06～0.12P、≤0.020S、0.25～0.50Cu、≤0.03Ti、0.01～0.04RE) 180mm×1200mm板坯由80t转炉-钢包吹氩-板坯连铸机生产。通过控制Cu/Ti≤20、P含量≤0.11%、RE含量0.01%～0.03%,使用09CuPTiRE钢专用保护渣,结晶器液面波动≤10mm,减少二冷配水量15%等工艺措施,使09CuPTiRE钢板坯纵裂发生率由15%降至0.5%。The 180 mm × 1 200 mm slab of atmospheric corrosion-resisting steel 09CuPTiRE （≤0. 12C, 0.06 - 0. 12P, ≤0. 020S, 0. 25-0. 50Cu,≤0. 03Ti, 0. 01-0. 04RE） is produced by 80 t converter - ladle argon stirring - vertical- bending slab caster process. With using improved process measures such as controlling Cu/Ti ≤ 20, P content 0. 11%, RE content 0. 01% - 0. 03%, using special mold powder for steel 09CuPTiRE, mold liquid level fluctuation ≤10 mm and decreasing secondary cooling water rate, the occurred rate of longitudinal crack of steel 09CuPTiRE decreased from original 15% to 0. 5%.

关 键 词：耐候钢09CuPTiRE 连铸板坯 纵裂 工艺改进 

分 类 号：TF777[冶金工程—钢铁冶金]