用电解着色技术在铝阳极氧化膜中共沉积MoS_2粒子  

Preparation of Self- Lubricating Aluminum Anodizing Composite Film with Electrolytic Coloration

作　　者：杜爱林[1] 向军淮[2] 何向明[2] 

机构地区：[1]东华理工学院南昌校区机电系,江西南昌330013 [2]江西科技师范学院江西省材料表面工程重点实验室,江西南昌330013

出　　处：《材料保护》2007年第11期37-38,共2页Materials Protection

基　　金：江西省科技攻关资助项目([2005]224号);东华理工学院核资源与环境教育部重点实验室资助项目(051111)

摘　　要：利用电解着色技术对硫酸阳极氧化膜进行镍盐着色,使MoS2润滑性粒子同金属一起沉积于氧化膜孔隙之中。采用能谱法证实了氧化膜中Mo的存在,并测定了其含量。试验结果表明,在给定的工艺条件下,MoS2润滑性粒子进入了氧化膜孔隙之中,Mo元素在试样表面的含量为3.49%(原子分数)。The lubricating particles of MoS2 are able to be co- deposited into the pores of aluminium anodized film with metal nickel by electrolytic coloration after the aluminium anodizing process with sulfuric acid. The results showed that in the given condition the lubricating particles of MoS, had entered into the pores of aluminium anodized film and the content of Mo on the surface of anodizing the film was 3.49% (atomic fraction).

关 键 词：电解着色 阳极氧化膜 MOS2 共沉积 

分 类 号：TG177[金属学及工艺—金属表面处理]