有机蒙脱石的制备新方法及性能表征  

New Method about the Preparation and Property Characterization of Organic-montmorillonite

作　　者：徐光年[1] 乔学亮[1] 邱小林[2] 陈建国[1] 

机构地区：[1]华中科技大学材料成形与模具技术国家重点实验室 [2]南昌理工学院纳米材料研究中心,南昌330013

出　　处：《硅酸盐通报》2007年第5期878-882,共5页Bulletin of the Chinese Ceramic Society

基　　金：安徽省教育厅自然科学基金项目(KJ2007B161)

摘　　要：四甲基氯化铵(TMA)、十六烷基三甲基溴化铵(CTAB)、双氯乙酸丙二醇酯基双十二烷基四甲基氯化二铵(双子季铵盐GQAS)作为钠基蒙脱石(Na-MMT)的改性剂,分别采用一次插层法和两次插层法对Na-MMT进行有机化改性。X射线衍射(XRD)测试表明,Na-MMT的层间距(d001)值随着改性剂碳链长度的增长而增大,采用一次插层法时,d001值依次由Na-MMT的1.30nm增大至1.34nm、2.89nm和3.72nm,而采用两次插层法时(第一次用TMA,第二次用双子季铵盐插层)OMMT的d001值增大至3.99nm。热重分析(TGA)表明Na-MMT的失重率为13.4%,双子季铵盐一次插层的有机MMT(OMMT)的失重率为40.5%,而用TMA第一次插层,双子季铵盐第二次插层的OMMT的失重率为49.8%.傅里叶变换红外光谱(FT-IR)同样证实采用两次插层法,MMT层间吸附的阳离子与有机阳离子的交换更彻底。用双子季铵盐作为改性剂、通过两次插层法制备OMMT,鲜见文献报道。Tetramethyl ammonium chloride （ TMA）, hexadecyl trimethyl ammonium bromide （ CTAB ） and bi-chloroacetic acid propylene glycol ester bi-dodecyl tetramethyl bi-ammonium chloride（gemini quaternary ammonium salt, abbreviate to GQAS） were applied to modifying agent of Na-montmorillonites（Na-MMT）, Na-MMT was modified by means of one and two times intercalated respectively. The results of X-ray diffraction（XRD） show that interlayer space （d001 ） of Na-MMT enhanced with the increasing of carbon chain long of the modifying agent, when one time intercalated way was used , the d001 value of Na-MMT increased from 1.30nm （Na-MMT） to 1.34nm for TMA,2.89nm for CTAB and 3.72nm for GQAS. When two times intercalated methods were applied （TMA intercalated first and GQAS second）, however,the d001 value of Na-MMT increased to 3.99nm. Thermogravimetric analysis（TGA） indicates the ratio of weight loss is 13.4% for Na-MMT,40. 5% for OMMT with one time intercalated, 49. 8% for OMMT with two times intercalated. Fourier transform infrared spectroscopy also confirms the exchange is more thoroughly between the cations adsorbed in interlayer of Na-MMT and the organic cations with two times intercalated methods. It is rarely found preparing OMMT by two times intercalated applying TMA and GQAS.

关 键 词：酯基双子季铵盐 插层 有机蒙脱石 XRD分析 性能 

分 类 号：TD985[矿业工程—选矿]