尿素嵌入法制备纤维素氨基甲酸酯的研究  

Study on Preparation of Cellulose Carbamate by Adding Urea

作　　者：哈丽丹.买买提 吾满江.艾力 

机构地区：[1]新疆大学化学化工学院,新疆乌鲁木齐830046 [2]中国科学院新疆理化研究所,新疆乌鲁木齐830016

出　　处：《合成纤维》2007年第6期24-27,共4页Synthetic Fiber in China

基　　金：国家科技部"西部开发"重大项目(2004BA901A22)。

摘　　要：探讨了尿素嵌入法制备纤维素氨基甲酸酯（CC）的生产工艺。指出：选用聚合度为450-625、α-纤维素含量大于90%的纤维素浆粕,用14%-16%的氢氧化钠溶液,于40-50℃条件下活化处理30-40min后,与尿素以1∶2-3的比例混合,在137℃的二甲苯体系中反应2-3h,便可得到含氮量为2.4%-3.5%的纤维素氨基甲酸酯产物。该产物在氢氧化钠溶液中可形成良好的稳定溶液,过滤性好,可直接用于纺丝。A process for manufacturing cellulose carbamate （CC） by adding urea was discussed. The cellulose pulp with or-cellulose higher than 90 % and polymerisation degree of range of 450-625 was treated with 14 %-16 % sodium hydroxide solution for 30-40 min under temperature of 40%-50%, and blended with urea in the ratio of 1：2-3. The product was reacted in xylene as solvent at 137℃ for 2-3 h. The stable solution of CC in sodium hydroxide solution with good filtration was obtained. The solution could be directly used for spinning.