Thermomechanical treatment of super high strength Cu-8.0Ni-1.8Si alloy  

作　　者：潘志勇 汪明朴 李周 肖柱 陈畅 

机构地区：[1]School of Materials Science and Engineering,Central South University [2]Key Laboratory of Nonferrous Metal Materials Science and Engineering,Ministry of Education, Changsha 410083,China

出　　处：《中国有色金属学会会刊：英文版》2007年第A02期1076-1080,共5页Transactions of Nonferrous Metals Society of China

基　　金：Project(20040533069) supported by Doctoral Fund of the Ministry of Education, China

摘　　要：The microstructures and properties of Cu-8.0Ni-1.8Si alloy subjected to different heat treatments were examined by mechanical and electrical properties measurements,optical and transmission electron microscopes observation. The results show that the precipitation process during aging can be accelerated by the cold deforming before aging. As the Cu-8.0Ni-1.8Si alloy is subjected to solution treatment at 970 ℃ for 4 h,cold rolling to 60% reduction,and then aging at 450 ℃ for 60 min,its properties are σb=1 050 MPa,σ0.2=786 MPa,δ=3.2% and conductivity 27.9%(IACS). The strengthening mechanisms of the alloy include spinodal decomposition strengthening,ordering strengthening and precipitation strengthening. The precipitation of the alloy is nano-scale Ni2Si phase.The microstructures and properties of Cu-8.0Ni-1.8Si alloy subjected to different heat treatments were examined by mechanical and electrical properties measurements, optical and transmission electron microscopes observation. The results show that the precipitation process during aging can be accelerated by the cold deforming before aging. As the Cu-8.0Ni-1.8Si alloy is subjected to solution treatment at 970 ℃ for 4 h, cold rolling to 60% reduction, and then aging at 450 ℃ for 60 min, its properties are σb=1 050 MPa, σ0.2=786 MPa, δ=3.2% and conductivity 27.9%（IACS）. The strengthening mechanisms of the alloy include spinodal decomposition strengthening, ordering strengthening and precipitation strengthening. The precipitation of the alloy is nano-scale Ni2Si phase.

关 键 词：超高强度合金 热机械处理 旋节线分解 铜镍硅合金 

分 类 号：TG166.2[金属学及工艺—热处理]