试件尺寸和养护温度对钢渣砂砂浆膨胀性能的影响  

Influence of specimen size and curing temperature on volume expansion of steel slag sand mortar

作　　者：伦云霞[1] 周明凯[1] 蔡肖[1] 陈美祝[1] 

机构地区：[1]武汉理工大学硅酸盐材料工程教育部重点试验室,湖北武汉430070

出　　处：《混凝土》2007年第11期4-5,共2页Concrete

基　　金：国家自然科学基金资助项目(50678139)

摘　　要：武钢转炉钢渣经自然冷却后,破碎磁选,过4.75 mm的筛,筛下的尾渣称为钢渣砂。采用此种钢渣砂配制砂浆,以硬化砂浆试体在水中的自由线性膨胀率为指标,研究了两种试件尺寸和50、80℃两种试验温度对钢渣砂砂浆膨胀性能的影响。试验结果表明:试件内温度场分布的不一致性是试件尺寸对膨胀率产生影响的主要原因;80℃试验温度不会改变砂浆性质,且与50℃相比,能加速钢渣砂的膨胀,起到快速检测的目的。Steel slag is a co-product from the conversion of iron to steel.After natural air cooled slag is crushed, magnetic screened and passed 4.75 mm sieves, the slag is called steel slag sand.This study investigated several factors influencing the volume expansion behavior of steel slag sand mortar.The results show that the uneven distribution of temperature field affects the linear volume expansion of different size mortars;compared with 50,80 ℃ curing temperature accelerates the volume expansion of steel slag mortar,without damaging the property of mortar.

关 键 词：钢渣砂砂浆 线性膨胀率 试件尺寸 养护温度 

分 类 号：TU528.041[建筑科学—建筑技术科学]