PET/TLCP共混物初生纤维的结构与性能  

STRUCTURE AND PROPERTIES OF PET/TLCP AS SPUN BLEND FIBERS

作　　者：梁伯润[1] 何小军[1] 陈稀[1] 屈凤珍 潘利华[1] 

机构地区：[1]中国纺织大学高分子材料工程系

出　　处：《高分子材料科学与工程》1997年第2期80-84,共5页Polymer Materials Science & Engineering

基　　金：国家自然科学基金;燕山石化研究院

摘　　要：研究了ＰＥＴ与热致液晶聚合物（ＴＬＣＰ）ＶｅｃｔｒａＡ９００共混物初生纤维的结构与性能以及热处理对它的影响。结果表明，初生纤维的取向与力学性质受纺丝拉伸比和共混物组成的影响，尤其是ＴＬＣＰ含量在１０％（质量）以上时，影响更为显著。Ｘ射线衍射结果证明，初生纤维基本为无定形结构。初生纤维最佳的热处理条件是在１８０℃处理２．５ｈ，处理后纤维的结晶度提高，力学性能明显改善。The structure and properties of the as spun fibers of PET blends with a thermotropic liquid crystalline polymer(TLCP), Vectra A900, has been studied. The annealing effect has also been examined for the as spun fibers. The results show that the orientation and the mechanical properties of the as spun fibers are strongly dependent on both the draw down ratio and the composition, especially for the blends with TLCP content up to 10 mass%. The WAXS results reveal a nearly amorphous state for the as spun blend fibers. An optimum annealing effect was attained at 180 ℃ for 2.5 h, from which an increase in crystallinity, consequently, a significant improvement of the mechanical properties was achieved for the as spun fibers.

关 键 词：液晶聚合物 共混物 聚对苯甲酸乙酯 复合纤维 

分 类 号：TQ342.94[化学工程—化纤工业]