Crystallization and Electrical Properties of (Ba_(0.4)Pb_(0.3))Sr_(0.3)TiO_3 Thin Film by Pulsed Laser Deposition  

作　　者：杨卫明 

机构地区：[1]Department of Electronic Science and Technology,Huazhong University of Science and Technology

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2007年第4期634-637,共4页武汉理工大学学报（材料科学英文版）

基　　金：the National Natural Science Foundation of China(No.60571009)

摘　　要：（Ba0.4Pb0.3）Sr0.3TiO3 thin films were fabricated via pulsed laser deposition （PLD） technique on Pt/TiO2/SiO2/Si substrate. The crystallization of the films was characterized by XRD and FSEM, and the experimental results suggested deposition parameters, especially the deposition temperature was the key factor in forming the perovskite structure. The dielectric properties of the film deposited with optimized parameters were studied by an Agilent 4294A impedance analyzer at 1 MHz. The dielectric constant was 772, and the loss tangent was 0.006. In addition, the well-shaped hysteresis loop also showed that the film had a well performance in ferroelectric. The saturated polarization P, remnant polarization Pr and coercive field E were about 4.6 μC/cm2, 2.5 μC/cm2 and 23 kV/cm （the coercive voltage is 0.7 V）, respectively. It is suggested the film should be a promising candidate for microwave applications and nonvolatile ferroelectric random access memories （NvFeRAMs）.（Ba0.4Pb0.3）Sr0.3TiO3 thin films were fabricated via pulsed laser deposition （PLD） technique on Pt/TiO2/SiO2/Si substrate. The crystallization of the films was characterized by XRD and FSEM, and the experimental results suggested deposition parameters, especially the deposition temperature was the key factor in forming the perovskite structure. The dielectric properties of the film deposited with optimized parameters were studied by an Agilent 4294A impedance analyzer at 1 MHz. The dielectric constant was 772, and the loss tangent was 0.006. In addition, the well-shaped hysteresis loop also showed that the film had a well performance in ferroelectric. The saturated polarization P, remnant polarization Pr and coercive field E were about 4.6 μC/cm2, 2.5 μC/cm2 and 23 kV/cm （the coercive voltage is 0.7 V）, respectively. It is suggested the film should be a promising candidate for microwave applications and nonvolatile ferroelectric random access memories （NvFeRAMs）.

关 键 词：（Ba0.4Pb0.3）Sr0.3TiO3 thin film PLD dielectric properties ferroelectric properties 

分 类 号：TN249[电子电信—物理电子学]