Influence of Cr_2O_3 on the Structure and Property of Mg-Al Spinel Synthesized by Waste Slag in Aluminum Factory  

作　　者：吴任平 于岩 阮玉忠 刘升 

机构地区：[1]School of Materials Science and Engineering, Fuzhou University

出　　处：《Chinese Journal of Structural Chemistry》2007年第12期1455-1460,共6页结构化学（英文）

基　　金：Supported by the Natural Science Foundation of Fujian Province (No. T0750005);Science and Technology Developing Foundation of Fuzhou University (No. 2007-XQ-02)

摘　　要：Via the solid phase reaction, Mg-Al spinel has been synthesized by using industrial waste slag from aluminum factory, basic magnesium carbonate and a little amount of clay as the main raw materials. The influences of Cr2O3 mineralizer on crystalline structure, micro-morphology and properties of synthesized Mg-Al spinel are discussed. The synthesized product was characterized by using XRD and SEM, and the relative contents of each crystalline phase are calculated by relevant analytical software such as Philips plus, Rietveld quantification and so on. The experimental results show that a certain amount of Cr2O3 is helpful to the formation of Mg-Al spinel, and when the addition of Cr2O3 is 2.0%, Mg-Al spinel in the system exists in the form of solid solution （Mg0.68A10.32）（A10.84Mg0.16）2O4 whose content is the highest reaching 91%. Then the corresponding indexes of each property are as follows： water absorption 3.0%, apparent porosity 9.8%, bulk density 3.36 g·cm^3, and flexural strength 83.32 MPa. Therefore, we can confirm that the optimum addition of Cr2O3 mineralizer is 2.0%.Via the solid phase reaction, Mg-Al spinel has been synthesized by using industrial waste slag from aluminum factory, basic magnesium carbonate and a little amount of clay as the main raw materials. The influences of Cr2O3 mineralizer on crystalline structure, micro-morphology and properties of synthesized Mg-Al spinel are discussed. The synthesized product was characterized by using XRD and SEM, and the relative contents of each crystalline phase are calculated by relevant analytical software such as Philips plus, Rietveld quantification and so on. The experimental results show that a certain amount of Cr2O3 is helpful to the formation of Mg-Al spinel, and when the addition of Cr2O3 is 2.0%, Mg-Al spinel in the system exists in the form of solid solution （Mg0.68A10.32）（A10.84Mg0.16）2O4 whose content is the highest reaching 91%. Then the corresponding indexes of each property are as follows： water absorption 3.0%, apparent porosity 9.8%, bulk density 3.36 g·cm^3, and flexural strength 83.32 MPa. Therefore, we can confirm that the optimum addition of Cr2O3 mineralizer is 2.0%.

关 键 词：Mg-Al spinel MINERALIZER crystalline phase cell parameter 