苯并噁嗪/环氧树脂基碳纳米管复合材料  

Composite of Benzoxazine,Epoxy and MWNT

作　　者：张凯[1] 徐日炜[1] 余鼎声[1] 

机构地区：[1]北京化工大学材料科学与工程学院北京市新型高分子制备与加工重点实验室,北京100029

出　　处：《合成材料老化与应用》2007年第4期1-5,共5页Synthetic Materials Aging and Application

基　　金：国家自然科学基金(50473041)

摘　　要：制备出一种新型的由苯并噁嗪、环氧树脂和碳纳米管(MWNT)组成的复合材料。对MWNT进行了表面改性,降低了苯并噁嗪和环氧树脂固化的温度,增强了MWNT与苯并噁嗪/环氧树脂基体间的结合力。对该复合体系进行了分步固化的研究。动态力学分析与热重分析表明由于MWNT的加入使得复合材料的储能模量和耐热性增加。通过断面扫描用SEM观察了MWNT在复合材料中的分散情况。A novel composite composed of benzoxazine, epoxy and multiwalled carbon nanotubes （MWNT） was prepared successfully. The surface modification of MWNT decreased the curing temperature of the system and improved the adhesion between MWNT, benzoxazine and epoxy. The step-curing of this system was researched. Dynamic mechanical analyses and Thermal gravity analyses indicated the storage modulus and heat resistance was improved. The dispersed MWNT inside composite was observed by SEM.

关 键 词：碳纳米管 苯并噁嗪 环氧树脂 

分 类 号：TQ323.1[化学工程—合成树脂塑料工业] O643[理学—物理化学]