铈钨坯的空心阴极等离子烧结工艺研究  

On Cerium-tungsten Alloy's Plasma Sintering Technology by Hollow Cathode Discharge

作　　者：牛宇锋[1] 王从曾[1] 马捷[1] 苏学宽[1] 张连宝[1] 

机构地区：[1]北京工业大学材料科学与工程学院,北京100022

出　　处：《中国钨业》2007年第6期25-28,共4页China Tungsten Industry

基　　金：国家"863"计划(2006AA03Z524);国家自然科学基金(50374003)

摘　　要：对空心阴极效应的发热机理及空心阴极等离子烧结铈钨坯工艺进行了初步研究。通过合理地控制电流、电压以及气压等影响因素,获得了持续稳定的空心阴极效应,使其阴极达到2500℃以上的高温。将此高温效应用于烧结高熔点材料——铈钨合金,获得了很好的效果。得到的铈钨烧结坯的密度达到17.8 g/cm3,与垂熔烧结方法获得的密度水平相当。The heating mechanism of hollow cathode effect and the technology of hollow cathode plasma sintering cerium-tungsten alloy adobes are researched. A constant and stable hollow cathode effect is achieved by regulating current, voltage, air pressure, with the temperature reaching as high as 2 500℃ or more in the hollow cathode. The high temperature is applied to sinter cerium-tungsten alloy, a high melting point material. The density of ceriumtungsten pieces after sintering reaches 17.8 g/cm^3, which is similar to the density by incipient fusion sintering technique.

关 键 词：空心阴极 烧结 等离子 铈钨合金 

分 类 号：TF124.5[冶金工程—粉末冶金]