硅酸铋粉体的制备与表征  

Preparation and Characterization of Bismuth Silicate Powders

作　　者：张争光[1] 王秀峰[1] 王莉丽[1] 田清泉[1] 

机构地区：[1]陕西科技大学材料科学与工程学院,西安710021

出　　处：《硅酸盐通报》2007年第6期1236-1239,共4页Bulletin of the Chinese Ceramic Society

摘　　要：以Bi2O3和SiO2为原料,采用机械合金化制备了硅酸铋(Bi12SiO20)的粉体。通过X射线衍射和扫描电子显微镜分析了合成粉体的相结构和形貌,研究了不同球磨时间对产物相组成的影响;并使用红外光谱分析和拉曼散射光谱对球磨得到的样品进行了分析。结果显示表明:球磨8h后出现了Bi12SiO20的晶相结构;随着球磨时间的延长促进了Bi12SiO20的形成,从而提供了一种可以商业化大规模生产Bi12SiO20压电粉体的方法。Bismuth silicate （Bi12SiO20, BSO） particles were prepared by the Mechanical alloying method using Bi2O3 and SiO2 as the starting materials. The milled BSO were studied by X-ray powder diffraction, scanning electron microscope, infrared and Raman scattering spectroscopy. After 8 hours of milling the formation of BSO was confirmed by X-ray powder diffraction. The infrared and Raman scattering spectroscopy results suggest that the increase of the milling time lead to the formation of nonferroelectric BSO, as seen by X-ray diffraction analysis. This milling process presents the advantage, that melting is not necessary, and the high efficiency of the process, opens a way to produce commercial amount of crystalline piezoelectric powders.

关 键 词：Bi12SiO20 机械合金化 光信息材料 

分 类 号：TN22[电子电信—物理电子学]