钻杆接头喷焊层耐磨带脱落原因及预防措施  

Reasons of wear-reistant zone dropout in spray-welding coating on drill pipe joint and its preventive measures

作　　者：田涛[1] 何小东[1] 杨红兵[1] 杨析[1] 

机构地区：[1]中国石油天然气集团公司管材研究所,西安市710065

出　　处：《焊接》2007年第12期41-43,共3页Welding & Joining

摘　　要：采用金相分析和扫描电镜分析方法,分析了钻杆接头喷焊耐磨带脱落原因。结果表明,基体金属与合金块间气孔和裂纹的存在是导致钻杆耐磨带在使用过程中脱落的主要原因,并结合喷焊工艺提出了预防措施。The causes of the wearable zone dropout were analyzed by the metallography analysis and SEM.The result shows that the porosity and crack between the base metal and the alloy block is the main cause of wear-resistant zone dropout during the lifespan,and the preventive measures had been proposed from the welding process.

关 键 词：钻杆接头 喷焊 耐磨带 

分 类 号：TG115.28[金属学及工艺—物理冶金]