Fe-28Mn-3Si-3Al TWIP钢变形过程中的孪晶观察  

Twins Observation During Deformation of Fe-28Mn-3Si-3Al TWIP Steel

作　　者：米振莉[1] 唐荻[1] 江海涛[1] 代永娟[1] 王海全[1] 

机构地区：[1]北京科技大学高效轧制国家工程研究中心,北京100083

出　　处：《钢铁》2007年第12期73-76,共4页Iron and Steel

基　　金：国家自然科学基金资助项目(50575022);高等学校博士学科点专项科研基金(20040008024)

摘　　要：采用扫描电镜、透射电镜对TWIP钢的拉伸变形过程中的孪晶进行了观察。研究结果表明,在TWIP钢的拉伸过程中,具有孪晶界的晶粒内部首先发生变形,并产生一定程度的加工硬化,随后其余部分晶粒发生转变,形成对变形有利的取向,从而变形得到扩展,最终得到非常大的无颈缩延伸;并且最先变形孪晶遗传了退火孪晶的取向。变形过程中孪晶和位错相互作用、孪晶和孪晶相互作用以及孪晶取向改变引发的滑移是使TWIP钢得到强化的主要变形机制。The microstructure of Twinning Induced Plasticity （TWIP） steel during tensile deformation was investigated with SEM and TEM. The results showed that the twins deformed firstly with work-hardening, then other grains turn to favorable orientation to complete further deformation. This deformation mechanism of twinning induced plasticity provides excellent elongation with no-necking phenomenon. The orientations of first deformed twins are transferred to annealing twin＇s hereditarily. The twin-twin interaction, the twin-dislocation interaction and the twin-sliding interaction play an important role during deformation. Key

关 键 词：TWIP钢 微观组织 变形孪晶 机制 

分 类 号：TG142.15[一般工业技术—材料科学与工程]