纳米钨粉制备的一种新方法  

A novel process for prepering tungsten nano-powder

作　　者：孙雯[1] 余世鑫[1] 

机构地区：[1]武汉工程大学化工与制药学院绿色化工过程省部共建教育部重点实验室湖北省新型反应器与绿色化学工艺重点实验室,湖北武汉430074

出　　处：《武汉工程大学学报》2008年第1期17-19,共3页Journal of Wuhan Institute of Technology

摘　　要：简要介绍纳米钨粉制备的一种新方法，在特殊混合和蒸发条件下先制备超细颗粒的APT，经500℃煅烧氧化制成黄钨，在600℃2氢还原制成纳米钨粉．制成的纳米钨粉比表面积BET-s为7．6m^2／g，TEM检测显示颗粒的粒径为40～80nm，XRD检测测算晶粒的粒径为32nm．A novel process for preparing tungsten nano-powder was briefly presented in this paper. Tungsten nano-powder has been prepared from superfinely grained APT crystalliized by particular mix and oxided at 500℃ ,and then reduced at 600℃in H2 atmosphere. The characteristics of the powders were studied and measured by EDXS, XRD, SEM and TEM. Fsss size and special surface area were also analyzed. The results show the average grain of the nano-powder was 32 nm （XRD-d） and the particle sizes for the nano-powder was 7. 6 m^2/g （BET-s）. The particle morphology from TEM indicates the particle sizes of the nano-powders were between 40 nm and 80 nm.

关 键 词：超细APT 超细黄钨 纳米钨粉 

分 类 号：TF125[冶金工程—粉末冶金]