SnO_2含量对AgSnO_2电接触材料组织与性能的影响  

Effect of Content of Tin-oxide on Structure and Property of AgSnO_2 Electrical Contact Material

作　　者：马战红[1] 陈敬超[2] 任凤章[1] 

机构地区：[1]河南科技大学材料科学与工程学院,洛阳471003 [2]昆明理工大学材料与冶金工程学院,昆明650093

出　　处：《材料导报》2007年第F11期348-349,356,共3页Materials Reports

基　　金：国家科技攻关(2001BA326C);河南科技大学科学研究基金(2003QN28)资助项目

摘　　要：采用粉末冶金法制备出银氧化锡电接触材料,研究了不同含量的氧化锡对材料组织性能的影响,随着氧化锡含量的增加,材料的导电率和抗熔蚀性能越来越差。在氧化锡含量为5wt%和8wt%时材料的性能相差较小,电接触性能较好。从降低成本及不降低材料性能来说,最佳氧化锡含量为8wt%。Silver tin oxide electrical contact material is prepared with powder metallurgic method. The material structure property is researched with different tin oxide contens. The material conductivity and fusibility resistance decrease in company with tin oxide increasing. The material performance discrepancy is on the small side when tin oxide contents are 5wt% and 8wt% respectively, and the electrical contact performances are satisfactory. The result is that the optimal content of tin oxide is 8wt% considering reduction of cost and maintaining material property.

关 键 词：电接触材料 氧化锡含量 组织 性能 

分 类 号：TM241[一般工业技术—材料科学与工程] TG146.2[电气工程—电工理论与新技术]