7055超高强、超高韧铝合金力学性能分析  

Mechanical properties of 7055 ultrahigh-strength and ultrahigh-ductility aluminum alloy

作　　者：李春梅[1] 陈志谦[1] 程南璞[1] 曾苏民[1] 何洪[1] 

机构地区：[1]西南大学材料科学与工程学院,重庆400715

出　　处：《金属热处理》2008年第1期100-104,共5页Heat Treatment of Metals

基　　金：西南师范大学青年基金项目(SWNUQ2005002SWNUQ2005001)

摘　　要：用拉伸试验研究了经不同固溶和时效工艺处理后7055铝合金的力学性能,并结合显微组织进行了分析。结果表明,复合固溶（双级）＋特殊时效处理新工艺比传统热处理工艺更合理,可使铝合金获得超高强、超高韧的有效结合。试验确定了最佳工艺,即强化固溶：455℃×（10-30）min＋470℃×（20-40）min＋（480-500）℃×（10-30）min;特殊时效：135℃×16 h＋（190-210）℃/（10-20）min,铝合金新状态T78的σb=720 MPa、σ0.2=690 MPa、δ5=12%。The mechanical properties of 7055 aluminum alloy under different solutions and aging conditions were investigated with tensile test and microstructures analyzing. The results show that the new heat treatment process combining compound solutions （2 steps） with a special aging process is more rational than the conventional process, as it can make the aluminum alloy to obtain ultrahigh-strength and ultrahigh-ductility. The test has determined the best solution and aging process for T78 of 7055 aluminum alloy is the intensifying solutions 455℃ × （ 10 -30）min ＋ 470 ℃ × （20 -40） min ＋ （480 - 500） ℃ ×（ 10 -30 ） min and special aging 135 ℃ ×16h ＋ （ 190 - 210 ） ℃ / （ 10 - 20 ） min） ： σb = 720 MPa,σ0.2 =690 MPa,85 = 12%.

关 键 词：7055铝合金 超高强 超高韧 

分 类 号：TG166.3[金属学及工艺—热处理]