Quantificational indexes for design and evaluation of copper staves for blast furnaces  

作　　者：Liang Qian Susen Cheng Hongbo Zhao 

机构地区：[1]School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China [2]Continuous Casting Technology Engineering Co. Ltd., MCC Group, Beijing 100081, China

出　　处：《Journal of University of Science and Technology Beijing》2008年第1期10-16,共7页北京科技大学学报（英文版）

基　　金：the National Natural Science Foundation of China(No.60672145).

摘　　要：The quantificational and normative design is the precondition of improving the design of copper staves for blast furnaces. Based on a 3-dimensional temperature field calculation model, from the view point of heat transfer and long campaigns note with the core of forming accretion, the forming-accretion-ability （FAA） and the rib hot surface maximum temperature difference （ATmax） as quantificational indexes to direct and evaluate the design of copper staves for blast furnaces were presented. The application of the two indexes in design essentially embodies the new long campaigns in the stage of design. With the application of the two indexes, good results can be obtained. Firstly, it was suggested that the rib height of a copper stave can be reduced to 15 mm, which is a new method and theory for the reduction of copper staves. Secondly, the influence of insert on FAA and ATmax, is decided by the volume of insert. According to this, the principle of design for the hot surface geometry of copper staves was put forward that the ratio of the rib hot surface to the copper stave hot surface （abbreviated as the ratio of rib to stave） must be maintained in the range of 45% to 55%; for the present copper stave with a 35-40 mm thick rib, the ratio of rib to stave in the range of 50% to 55% can optimize the design of copper staves; for the copper stave with a smaller rib thickness, for example 15 ram, the ratio of rib to stave in the range of 45% to 50% can optimize the design of copper staves. It can be summarized that the thicker the rib thickness, the larger is the ratio of rib to stave. 2008 University of Science and Technology Beijing. All rights reserved.The quantificational and normative design is the precondition of improving the design of copper staves for blast furnaces. Based on a 3-dimensional temperature field calculation model, from the view point of heat transfer and long campaigns note with the core of forming accretion, the forming-accretion-ability （FAA） and the rib hot surface maximum temperature difference （ATmax） as quantificational indexes to direct and evaluate the design of copper staves for blast furnaces were presented. The application of the two indexes in design essentially embodies the new long campaigns in the stage of design. With the application of the two indexes, good results can be obtained. Firstly, it was suggested that the rib height of a copper stave can be reduced to 15 mm, which is a new method and theory for the reduction of copper staves. Secondly, the influence of insert on FAA and ATmax, is decided by the volume of insert. According to this, the principle of design for the hot surface geometry of copper staves was put forward that the ratio of the rib hot surface to the copper stave hot surface （abbreviated as the ratio of rib to stave） must be maintained in the range of 45% to 55%; for the present copper stave with a 35-40 mm thick rib, the ratio of rib to stave in the range of 50% to 55% can optimize the design of copper staves; for the copper stave with a smaller rib thickness, for example 15 ram, the ratio of rib to stave in the range of 45% to 50% can optimize the design of copper staves. It can be summarized that the thicker the rib thickness, the larger is the ratio of rib to stave. 2008 University of Science and Technology Beijing. All rights reserved.

关 键 词：blast furnace （BF） copper stave quantificational index forming-accretion-ability 

分 类 号：TF321[冶金工程—冶金机械及自动化]