NiCrWRE合金粉末喷熔层和SAE52100球-盘摩擦副摩擦性能研究  

Tribological properties of NiCrWRE coatings coupling with SAE52100 steel under ball-disc reciprocating sliding

作　　者：梁补女[1] 张振宇[1] 张鹏林[2] 

机构地区：[1]兰州工业高等专科学校机械工程系,兰州730050 [2]兰州理工大学甘肃省省部共建有色金属新材料国家重点实验室,兰州730050

出　　处：《粉末冶金技术》2008年第1期19-22,29,共5页Powder Metallurgy Technology

基　　金：甘肃省自然基金资助项目(0710RJZA071)

摘　　要：在45#钢表面制备了NiCrWRE合金粉末喷熔层,利用球-盘摩擦试验,进行了NiCrWRE合金粉末喷熔层与SAE52100钢球的干摩擦磨损试验研究。结果表明:NiCrWRE合金喷熔层具有良好的耐磨性和较低的摩擦系数,在低速轻载条件下,镍基合金喷熔层的磨损机理为微观切削;高速重载时,表现为粘着磨损和磨料磨损,喷熔层表面形成了致密的氧化物膜,有效地降低了磨损率。NiCrWRE alloy powders were thermally sprayed on to a 45 carbon steel substrate. Tribological and wear properties of coatings were tested under SRV reciprocating sliding test （ball-disc contact）. The results show that friction coefficient and wear rates of NiCrWRE alloy coatings are lower. The wear mechanism of NiCrWRE alloy coatings is micro-plowing at low sliding speed and light load, and then transforms to adhesive wear and abrasive wear at high sliding speed and heavier load. It is concluded that the oxidizing film formed on the worn surface makes a contribution to an increase in the coating wear resistance.

关 键 词：NiCrWRE 喷熔层 球-盘摩擦试验 滑动磨损 耐磨机理 

分 类 号：TF123.71[冶金工程—粉末冶金] TH117.1[冶金工程—冶金物理化学]