Effects of heat treatment on the properties of powder injection molded AlN ceramics  

作　　者：DU Xueli QIN Mingli Akhtar Farid FENG Peizhong QU Xuanhui 

机构地区：[1]Institute of Powder Metallurgy, University of Science and Technology Beijing, Beijing 100083, China [2]School of Materials Science andEngineering, Tianjin University of Technology, Tianjin 300191, China

出　　处：《Rare Metals》2008年第1期70-73,共4页稀有金属（英文版）

基　　金：supported by the National Natural Science Foundation of China(Nos.50025412 and 60576011);the National Key Basic Research and Development Program of China(No.TG2000067203).

摘　　要：The effects of two different heat-treatment atmospheres,nitrogen atmosphere and reducing nitrogen atmosphere with carbon,on the properties of Y2O3-doped aluminum nitride（AlN） ceramics were investigated.The AlN powder as a raw material was synthesized by self-propagating high-temperature synthesis（SHS） and compacts were fabricated by employing powder injection molding technique.The polymer-wax binder consisted of 60 wt.% paraffin wax（PW）,35 wt.% polypropylene（PP）,and 5 wt.% stearic acid（SA）.After the removal of binder,specimens were sintered at 1850°С in nitrogen atmosphere under atmospheric pressure.To improve the thermal conductivity,sintered samples were reheated.The result reveals that the heat-treatment atmosphere has significant effect on the properties and secondary phase of AlN ceramics.The thermal conductivity and density of AlN ceramics reheated in nitrogen gas are 180 W·m^-1·K^-1 and 3.28 g·cm^-3 and the secondary phase is yttrium aluminate.For the sample reheated in reducing nitrogen atmosphere with carbon,the thermal conductivity and density are 173 W·m^-1·K^-1 and 3.23 g·cm^-3,respectively,and the secondary phase is YN.The effects of two different heat-treatment atmospheres,nitrogen atmosphere and reducing nitrogen atmosphere with carbon,on the properties of Y2O3-doped aluminum nitride（AlN） ceramics were investigated.The AlN powder as a raw material was synthesized by self-propagating high-temperature synthesis（SHS） and compacts were fabricated by employing powder injection molding technique.The polymer-wax binder consisted of 60 wt.% paraffin wax（PW）,35 wt.% polypropylene（PP）,and 5 wt.% stearic acid（SA）.After the removal of binder,specimens were sintered at 1850°С in nitrogen atmosphere under atmospheric pressure.To improve the thermal conductivity,sintered samples were reheated.The result reveals that the heat-treatment atmosphere has significant effect on the properties and secondary phase of AlN ceramics.The thermal conductivity and density of AlN ceramics reheated in nitrogen gas are 180 W·m^-1·K^-1 and 3.28 g·cm^-3 and the secondary phase is yttrium aluminate.For the sample reheated in reducing nitrogen atmosphere with carbon,the thermal conductivity and density are 173 W·m^-1·K^-1 and 3.23 g·cm^-3,respectively,and the secondary phase is YN.

关 键 词：powder injection molding AIN ceramics heat treatment thermal conductivity 

分 类 号：TG15[金属学及工艺—热处理]