Microstructures and magnetic properties of [SiO_2/FePt]_5/Ag thin films  

作　　者：范九萍 许小红 江凤仙 田宝强 武海顺 

机构地区：[1]School of Chemistry and Materials Science, Shanxi Normal University

出　　处：《Journal of Central South University of Technology》2008年第1期11-14,共4页中南工业大学学报（英文版）

基　　金：Project(10574085) supported by the National Natural Science Foundation of China;Project(207020) supported by the Science Technology Key Project of the Ministry of Education, China

摘　　要：[SiO2/FePt]5/Ag thin films were deposited by RF magnetron sputtering on the glass substrates and post annealing at 550 ℃ for 30 min in vacuum. Vibrating sample magnetometer and X-ray diffraction analyser were applied to study the magnetic properties and microstructures of the films. The results show that without Ag underlayer [SiO2/FePt]5 films deposited onto the glass are FCC disordered; with the addition of Ag underlayer [SiO]FePt]5/Ag films are changed into L10 and （111） mixed texture. The variation of the SiO2 nonmagnetic layer thickness in [SiO2/FePt]5/Ag films indicates that SiO2-doping plays an important role in improving the order parameter and the perpendicular magnetic anisotropy, and reducing the grain size and intergrain interactions. By controlling SiO2 thickness the highly perpendicular magnetic anisotropy can be obtained in the [SiO2 （0.6 nm）/FePt （3 nm）]5/Ag （50 nm） films and highly （001）-oriented films can be obtained in the [SiO2 （2 nm）/FePt （3 nm）]5/Ag （50 nm） films.[SiO2/FePt]5/Ag thin films were deposited by RF magnetron sputtering on the glass substrates and post annealing at 550 ℃ for 30 min in vacuum. Vibrating sample magnetometer and X-ray diffraction analyser were applied to study the magnetic properties and microstructures of the films. The results show that without Ag underlayer [SiO2/FePt]5 films deposited onto the glass are FCC disordered; with the addition of Ag underlayer [SiO2/FePt]5/Ag films are changed into L10 and (111) mixed texture. The variation of the SiO2 nonmagnetic layer thickness in [SiO2/FePt]5/Ag films indicates that SiO2-doping plays an important role in improving the order parameter and the perpendicular magnetic anisotropy, and reducing the grain size and intergrain interactions. By controlling SiO2 thickness the highly perpendicular magnetic anisotropy can be obtained in the [SiO2 (0.6 nm)/FePt (3 nm)]5/Ag (50 nm) films and highly (001)-oriented films can be obtained in the [SiO2 (2 nm)/FePt (3 nm)]5/Ag (50 nm) films.

关 键 词：[SiO2/FePt]5 multilayer films SiO2-doping Ag underlayer （001） orientation 

分 类 号：TB383.2[一般工业技术—材料科学与工程]