超细粉体制备Nd∶Y2O3透明陶瓷  

Preparation of Transparent Nd∶Y_2O_3 Ceramic Using Ultrafine Powders

作　　者：霍地[1] 孙旭东[1] 刘亦农[2] 张牧[2] 修稚萌[1] 李晓东[1] 

机构地区：[1]东北大学材料各向异性与织构教育部重点实验室,辽宁沈阳110004 [2]西澳大利亚大学机械工程学院,Crawely WA 6009

出　　处：《中国稀土学报》2008年第1期56-60,共5页Journal of the Chinese Society of Rare Earths

基　　金：国家自然科学基金(50672014);辽宁省自然科学基金(20062019);国家杰出青年基金(50425413)资助项目

摘　　要：采用碳酸氢铵为沉淀剂合成了碱式碳酸钇沉淀前驱体,研究了的前躯体的煅烧工艺对氧化钇粉体性能及烧结氧化钇陶瓷组织、致密化行为以及透光率的影响。在1000℃煅烧6 h获得的超细粉体,经过在氢气介质中1750℃保温3 h烧结后,获得组织均匀,无残余气孔,透光率高的氧化钇陶瓷。Yttrium carbonate precursor was synthesized using ammonium hydrocarbonate as the precipitant. The effect of calcination process of the precursor on properties of the yttria powder and microstructure, densification behavior and light transmittance of the sintered Nd：Y2O3 ceramic was investigated. Using the ultrafine yttria powder obtained by calcining at 1000 ℃ for 6 h, dense and highly transparent Nd：Y2O3 ceramic with homogeneous microstructure and no residue pores was fabricated by sintering in hydrogen at 1750 ℃ for 3 h.

关 键 词：掺杂Nd3+氧化钇 透明陶瓷 超细粉体 煅烧温度 稀土 

分 类 号：TB321[一般工业技术—材料科学与工程] TF123[冶金工程—粉末冶金]