Effect of niobium on glass-formation ability and soft magnetic properties of Gd-doping glassy alloys  

作　　者：刘烜 丁艳红 赵水生 龙毅 叶荣昌 常永勤 

机构地区：[1]School of Materials Science and Engineering, University of Science and Technology Beijing

出　　处：《Journal of Rare Earths》2008年第1期89-92,共4页稀土学报（英文版）

基　　金：Project supported by the National Natural Science Foundation of China (50471094)

摘　　要：The effect of niobium on glass-formation ability and soft magnetic properties were studied in Fe-Gd-B glassy alloys. The glassy alloys exhibited high glass-formation ability when the element of Nb was added. Bulk glassy rod （Fe0.87Co0.13）68.5Gd3.5Nb3B25 with a diameter up to 3 mm was produced by copper mold casting. The size of the atom might play an important role in increasing glass-formation ability. The coercive force of glassy （Fe0.87Co0.13）71.5.xGd3.sNbxB25 （x=1.2, 1.5, 2, 2.5, 3, 4） alloys decreased after the addition of niobium element and was in the range of 1.5-2.9 A/m. The permeability spectrum of （Fe0.87Co0.13）70.3Gd3.5Nb1.5B25 glassy ribbon showed that the relaxation frequency （f0） was 6.1 MHz.The effect of niobium on glass-formation ability and soft magnetic properties were studied in Fe-Gd-B glassy alloys. The glassy alloys exhibited high glass-formation ability when the element of Nb was added. Bulk glassy rod （Fe0.87Co0.13）68.5Gd3.5Nb3B25 with a diameter up to 3 mm was produced by copper mold casting. The size of the atom might play an important role in increasing glass-formation ability. The coercive force of glassy （Fe0.87Co0.13）71.5.xGd3.sNbxB25 （x=1.2, 1.5, 2, 2.5, 3, 4） alloys decreased after the addition of niobium element and was in the range of 1.5-2.9 A/m. The permeability spectrum of （Fe0.87Co0.13）70.3Gd3.5Nb1.5B25 glassy ribbon showed that the relaxation frequency （f0） was 6.1 MHz.

关 键 词：iron-based glassy alloys glass-formation ability soft magnetic properties permeability spectrum rare earths 

分 类 号：TG139.8[一般工业技术—材料科学与工程]