MoO_3/DMMP/APP复合抑烟、阻燃聚氯乙烯的研究  

Study of MoO_3/DMMP/APP component on smoke suppression and flame retardant of PVC

作　　者：阎春绵[1] 张忠厚[1] 贾天刚[1] 

机构地区：[1]郑州轻工业学院材料与化学工程学院,河南郑州450002

出　　处：《郑州轻工业学院学报（自然科学版）》2008年第1期38-40,共3页Journal of Zhengzhou University of Light Industry:Natural Science

摘　　要：研究了MoO3/DMMP/APP三元复合体系对聚氯乙烯材料的抑烟、阻燃性能的影响.结果表明,复合材料的最佳配方为m(PVC)∶m(MoO3)∶m(DMMP)∶m(APP)=100∶3∶6∶8,此时材料的最大烟密度由100降低到74.36,烟密度等级由91.02降低到52.02,氧指数由45%提高到60%,拉伸强度为50.5 MPa,力学性能和阻燃性能均达到最大值.与纯PVC材料相比,复合材料的储能模量有较大程度的提高,而玻璃化转变温度则降低了1.34℃,失重温度范围变窄,最大失重温度降低了12℃,失重速率明显降低.The influence of MoO3/APP/DMMP component on flame retardance and smoke suppression were studied. The results showed that best formulation of composite materials were rn （ PVC ） ： m （ MoO3 ） ： m（DMMP）： m（APP） = 100： 3： 6： 8. The most smoke density decreased from 100 to 74.36, the smoke density rank decreased from 91.02 to 52.02, the limited oxygen index increased from 45% to 60%. The tensile strength were 50.5 MPa. Analysis results showed that accumulation energy was increased, vitrification point has reduced by 1.34 ℃, the temperature range of mass loss for PVC composite was obviously narrower than that the sample without MoO3/DMMP/APp component, the temperature of maximum mass loss decreased nearly 12 ℃, but the rate of mass loss decreased clearly.

关 键 词：聚氯乙烯 三氧化钼 甲基磷酸二甲酯 聚磷酸铵 抑烟 阻燃 

分 类 号：TQ320[化学工程—合成树脂塑料工业]