AZ91镁合金的热压缩行为(Ⅰ)--EBSP分析  

Hot compression behavior of AZ91 alloy(Ⅰ)——EBSP analysis

作　　者：刘六法[1] 丁汉林[1] 鎌土重晴 丁文江[1] 小島陽[2] 

机构地区：[1]上海交通大学轻合金精密成型国家工程研究中心,上海200030 [2]长岡技术科学大学机械系,日本新潟940-2188

出　　处：《中国有色金属学报》2008年第2期237-242,共6页The Chinese Journal of Nonferrous Metals

基　　金：国家自然科学基金资助项目(50505026);上海市自然科学基金资助项目(05ZR14075)

摘　　要：采用背散射电子衍射技术(EBSP)分析AZ91镁合金在热压缩变形过程中的流变行为及组织演变特征。研究表明,该合金在热压缩实验中通过动态再结晶过程细化基体晶粒。随应变速率降低,稳态组织的平均晶粒尺寸增大,大尺寸晶粒比例和大边数晶粒比例增加。流变曲线的峰值应力随Zener-Hollomon参数的增大而增大。The deformation behavior and microstructure evolution characteristics of the AZ91 magnesium alloy during hot compression process is studied by the electron back-scattered diffraction pattern （EBSP） approach. The results suggest that dynamic recrystalliztion （DRX） occurs during the compression process. The DRX in turn refines the grains. When the strain rate is decreased, the average grain size, the fractions of large-size grains and the fraction of large-side grains in the final microstructures are increased. The peak stress of the flow stress curve increases along with the increase of the Zener-Hollomon parameter.

关 键 词：AZ91合金 动态再结晶 流变行为 组织转变 

分 类 号：TG146.2[一般工业技术—材料科学与工程]