从无序到有序ZnO纳米棒的制备  

The synthesis of ZnO nanorods from out-of-order to order

作　　者：刘然[1] 章婷[1] 赵谡玲[1] 徐征[1] 张福俊[1] 李远[1] 宋林[1] 徐叙瑢[1] 

机构地区：[1]北京交通大学光电子技术研究所发光与光信息技术教育部重点实验室,北京100044

出　　处：《功能材料》2008年第3期488-489,493,共3页Journal of Functional Materials

基　　金：国家重点基础研究发展计划(973计划)资助项目(2003CB314707);国家自然科学基金重点资助项目(10434030);国家高技术研究发展计划(863计划)资助项目(2006AA03Z0412);国家自然科学基金资助项目(10774013;60576016);北京市自然科学基金资助项目(2073030);北京交通大学客座研究员基金资助项目(48107)

摘　　要：采用3种不同的方法在氧化铟锡玻璃衬底上沉积一层ZnO纳米晶薄膜,然后采用改进的水热法在制备有ZnO纳米晶薄膜的衬底上生长ZnO纳米棒,实现了纳米棒从无序到有序的生长。从XRD和SEM图可得,有序的纳米棒沿(002)择优取向,基本与衬底垂直,平均直径约为40nm。In the paper, three different methods were adopted to deposit a layer ot ZnO trim on the mature tm oxide substrates, then put the substrates into the precursor solution to synthesis the ZnO nanorods, implement the growth of nanorods from out-of-order to order. The SEM and XRD indicate that the ordered ZnO nanorods mainly have c axis orientation, and most of them were vertical to the substrates. The average diameter was 40nm.

关 键 词：ZnO纳米晶薄膜 改进的水热法 ZNO纳米棒 有序 

分 类 号：TN304.2[电子电信—物理电子学] O782.1[理学—晶体学]