三维原子探针对微合金钢中G．P．区的观测  

Three dimensional atom probe observation of G.P.zone in micro-alloyed steel

作　　者：刘文庆[1] 刘庆冬[1] 李聪 方淑芳[3] 周邦新[1] 

机构地区：[1]上海大学分析测试中心,上海200444 [2]中科华核电技术研究院,江苏苏州215004 [3]攀枝花钢铁研究院,四川攀枝花617000

出　　处：《江苏大学学报（自然科学版）》2008年第2期131-133,共3页Journal of Jiangsu University：Natural Science Edition

基　　金：上海市科委纳米专项(0552nm049)

摘　　要：对Nb-V微合金钢进行模拟控轧控冷试验,利用光学显微镜、场离子显微镜、三维原子探针等测试分析技术和手段,研究铁素体基体中碳化物析出早期阶段的特点.用三维原子探针研究基体中碳化物的析出过程,发现在NbC析出初期,C和Nb原子在铁素体同一个(001)原子面上发生偏聚,且质量分数都不到5%,认为这是在基体中形成的G.P.区.By applying the techniques of optical microscope, field ion microscope （FIM） and three-dimensional atom probe （3 DAP） , the carbides precipitated from ferrite matrix on the early stage of niobium and vanadium micro-alloyed steels were characterized. 3DAP was carried out to investigate the carbides precipitate process in niobium and vanadium micro-alloyed steels. Niobium and carbon atoms segregating at a ferrite matrix （001） plane and the concentration of less than 5% were observed in the matrix during the initial precipitating stages of NbC. The monolayer enrichment zone of niobium and carbon atoms was considered as G.P. zone.

关 键 词：微合金钢 G.P.区 三维原子探针 NbC析出 偏聚 

分 类 号：TG113.25[金属学及工艺—物理冶金]