低温固相合成牙用白榴石  

LOW-TEMPERATURE SOLID-PHASE SYNTHESIS DENTAL LEUCITE

作　　者：陈堃[1,2] 滕元成[1] 康明[1,3] 齐晓敏[1] 孙致平[4] 曾冲盛[1] 徐会杰[1] 

机构地区：[1]西南科技大学材料科学与工程学院 [2]福建省出入境检验检疫局,福州350001 [3]四川大学材料学院,成都610064 [4]马鞍山钢铁股份有限公司技术中心

出　　处：《中国陶瓷》2008年第4期52-55,共4页China Ceramics

基　　金：四川省教育厅重点项目(编号:2006A094)

摘　　要：以钾长石、碳酸钾等为主要原料,固相合成白榴石晶体。通过实验发现提高配方中碱性氧化物K2O的含量,减低酸性氧化物SiO2的含量可以显著减低白榴石的合成温度。实验表明:按照白榴石的化学组成进行配比时,配方在1100℃就完全转化成白榴石,比传统白榴石的转化温度减低了约100℃,其在1100℃下合成时热膨胀系数为27.9×10-6/K(30-700℃),平均晶粒尺寸为15μm。The leucite crystal is synthesized using by K-feldspar and potassium as main raw material. we found that improved formulations basic oxide K20 content and reduce acidic oxide SiO2 content can significantly reduce leucite the synthesis temperature.The results that the formula accord to leucite chemical composition ratio completely can be transformed into leucite in 1000℃ ,which less than traditional solid-phase synthesis of leucite reduce the synthesis temperature of about 200 ℃, its calculated coefficients of thermal expansion（30-700℃ ）reached 27.9×10^-06/K, and its tile average cystal size of 15μ m.

关 键 词：白榴石 热膨胀系数 钾长石 固相合成 

分 类 号：TQ171[化学工程—玻璃工业] TB383[化学工程—硅酸盐工业]