EG与DBDPE/Sb_2O_3复合阻燃ABS热失重行为研究  

STUDY ON THERMOGRAVIMETRIC BEHAVIOR OF FLAME RETARDANT ABS BY EG/DBDPE/Sb_2O_3

作　　者：王扬利[1] 李荣勋[1] 孙立水[1] 刘莉[1] 李少香[1] 刘光烨[1] 

机构地区：[1]青岛科技大学新材料研究重点实验室,青岛266042

出　　处：《工程塑料应用》2008年第4期55-59,共5页Engineering Plastics Application

摘　　要：采用可膨胀石墨(EG)与十溴二苯乙烷(DBDPE)、三氧化二锑(Sb2O3)复合阻燃(丙烯腈/丁二烯/苯乙烯)共聚物(ABS),通过热重分析研究了阻燃ABS体系的热失重行为。结果表明,DBDPE/Sb2O3改变了ABS的热降解历程,以气相阻燃机理为主;EG对ABS的热降解历程影响不大,形成的炭层有利于阻燃,以凝聚相阻燃机理为主;两者复配可同时在气相和凝聚相起作用,使得ABS的峰值热失重速率均大幅下降,阻燃ABS的极限氧指数可达30%,EG与DBDPE/Sb2O3复合对ABS阻燃具有一定的协同阻燃效应。EG, DBDPE and Sb203 are used to prepare flame retardant ABS, and the thermogravimetric behavior of flame retardant ABS is analyzed by thermogravimetry. The results show that the degrading process of ABS is changed by adding DBDPE/ Sb2O3 , and the acting mechanism is gas phase antiflaming; EG has little effect on the degrading process of ABS, and the mechanism is condense phase antiflaming. The synergy of EG and DBDPE/Sb2O3 can significantly decrease the peak decomposition rate of ABS, with the LOI of flame retardant ABS reaching 30%.

关 键 词：可膨胀石墨 十溴二苯乙烷 阻燃 (丙烯腈/丁二烯/苯乙烯)共聚物 热失重 

分 类 号：TQ325.2[化学工程—合成树脂塑料工业] TQ323.4