新型可溶性含氟聚芳醚酮的合成、表征及性能  

Synthesis,Characterization and Properties of Novel Soluble Poly (ether ether ketone) Containing Fluorin Structure

作　　者：张鹏[1] 刘新才[1] 李鹏[1] 周宏伟[1] 陈春海[1] 

机构地区：[1]吉林大学麦克德尔米德实验室,长春130012

出　　处：《高等学校化学学报》2008年第4期865-867,共3页Chemical Journal of Chinese Universities

基　　金：国家'九七三'计划(批准号:G2003CB615604);吉林省杰出青年基金资助

摘　　要：The novel and soluble poly(ether ether ketone)(PEEK)containing fluorin structure(6F-PEEK)was prepared by nucleophilic reaction of 4,4’-difluorobenzophenone,bisphenol A and hexafluobisphenol A in the presence of anhydrous K2CO3 with tetramethylene sulfone as the solvents.The molecular weight of the polymer was determined by GPC.The structure of the polymer was characterized by FTIR,1H NMR and 19F NMR spectroscopies.The glass transition temperature and the temperature for 5% mass loss of 6F-PEEK were 153 and 493 ℃,respectively.The polymer exhibits an excellent thermal stability,mechanical property and solubility.The rate of elongation at break,tensile strength and tensile modulus of 6F-PEEK were 55.2%,66 MPa,and 2.13 GPa,respectively.The novel and soluble poly（ ether ether ketone） （PEEK） containing fluorin structure （6F-PEEK） was prepared by nucleophilic reaction of 4,4＇-difluorobenzophenone, bisphenol A and hexafluobisphenol A in the presence of anhydrous K2CO3 with tetramethylene sulfone as the solvents. The molecular weight of the polymer was determined by GPC. The structure of the polymer was characterized by FTIR,^1H NMR and 19F NMR spectroscopies. The glass transition temperature and the temperature for 5% mass loss of 6F-PEEK were 153 and 493 ℃, respectively. The polymer exhibits an excellent thermal stability, mechanical property and solubility. The rate of elongation at break, tensile strength and tensile modulus of 6F-PEEK were 55.2%, 66 MPa, and 2. 13 GPa, respectively.

关 键 词：聚醚醚酮 六氟双酚A 含氟聚合物 可溶性聚醚醚酮 

分 类 号：O631[理学—高分子化学]