超声波对纳米Ni-TiN复合镀层的影响  

Effect of ultrasonic wave on nano Ni-TiN composite coatings

作　　者：夏法锋[1] 吴蒙华[2] 贾振元[1] 李智[2] 

机构地区：[1]大连理工大学机械工程学院,辽宁大连116023 [2]大连大学机械工程学院,辽宁大连116622

出　　处：《功能材料》2008年第4期690-691,694,共3页Journal of Functional Materials

基　　金：国家自然科学基金资助项目(50475108);辽宁省自然科学基金资助项目(20042123)

摘　　要：采用超声-电沉积的方法制备纳米Ni-TiN复合镀层。利用原子吸收分光光度计(AAS)、高分辨率电子显微镜(HRTEM)和X射线衍射仪(XRD)研究超声波对复合镀层含量、显微组织及微观结构的影响。结果表明,超声波的引入,不仅能提高复合镀层中纳米TiN粒子的含量,还能明显改善显微组织结构,细化晶粒。在超声波功率为200W时,镀层中粒子含量达到最大值9.9%。Nano Ni-TiN composite coatings were prepared by ultrasonie-electrodepositing method. The effect of ultrasonic wave on the content, morphology and mierostrueture were studied by the atomic absorption speetrophotometer （AAS）, high respective transmission electron microscope （HRTEM） and X-ray diffraction analysis （XRD）. The result shows that the join of ultrasonic wave, which not only increase the content of nano TiN partieles in composite coatings, but also improve the morphology obviously and have a fine mierostrueture. When the ultrasonic power is 200W, the content reaches 9.9%.

关 键 词：超声波 复合镀层 影响 

分 类 号：TG153.43[金属学及工艺—热处理]