机构地区:[1]安徽建筑工业学院材料科学与工程系,安徽合肥230022
出 处:《合肥工业大学学报(自然科学版)》2008年第4期600-602,共3页Journal of Hefei University of Technology:Natural Science
基 金:安徽省教育厅自然科学基金资助项目(kj2008b273)
摘 要:文章采用聚丙烯酰胺水凝胶为模板,以Na2 siO3作为SiOx的硅源,通过控制聚丙烯酰胺水凝胶模板中Na2 SiO3溶液的浓度,合成了可变粒径的SiOx晚粒子,其粒径范围分别为220~250nm、160~190nm和10-20nm;并通过场发射扫描电镜(FSEM)、透射电镜(TEM)、X射线光电子能谱(XPS)及红外光谱(IR)等对所制备的SiOx纳米粒子的形貌和成分进行表征。The amorphous SiOx nanoparticles with various diameters (220-250 nm, 160-190 nm and 10-20 nm) were synthesized. The preparation method was based on hydrolyzation induced self-assembly with Na2SiO3 as the silica precursor and the polyacrylamide gels as template. The morphology and composition of the obtained SiOxnanoparticles were investigated by field scanning electron microscopy (FSEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS) and infrared spectrum (IR).
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在载入数据...
正在链接到云南高校图书馆文献保障联盟下载...
云南高校图书馆联盟文献共享服务平台 版权所有©
您的IP:216.73.216.145