剥离型(苯乙烯/马来酸酐)共聚物/蒙脱土纳米复合材料的制备  

PREPARATION OF EXFOLIATED POLY(STYRENE/MALEIC ANHYDRIDE)/MONTMORILLONITE NANOCOMPOSITES

作　　者：陆昶[1] 邢艳艳[1] 田炳坤[1] 彭淑鸽[1] 刘继纯[1] 张玉清[1] 

机构地区：[1]河南科技大学化工与制药学院,洛阳471003

出　　处：《工程塑料应用》2008年第5期14-17,共4页Engineering Plastics Application

摘　　要：研究了制备剥离型(苯乙烯/马来酸酐)共聚物(SMAH)蒙/脱土(MMT)纳米复合材料的方法。研究表明,通过原位插层及熔融插层只能制备出插层型的SMAH/MMT纳米复合材料。为了制备剥离型的SMAH/MMT纳米复合材料,先将尼龙6(PA6)与MMT熔融插层制备出PA6/MMT纳米复合材料,再用抽提的方法将PA6/MMT复合材料中的部分PA6除去,得到含有少量PA6的剥离型MMT,然后将剥离型MMT与SMAH共混,从而制备出剥离型的SMAH/MMT纳米复合材料。该复合材料的粘度低于SMAH,且具有较好的加工性能。The way to prepare exfoliated SMAH/MMT nanocomposites was studied. The results showed that intercalated SMAH/MMT nanocomposites could be prepared by in-situ intercalation and melt intercalation. In order to prepare exfoliated SMAH/ MMT nanocomposites, the exfoliated MMT was obtained by extracting part PA6 from PA6/MMT nanocomposites prepared by melt intercalation. Then blending the exfoliated MMT and SMAH could obtain the exfoliated SMAH/MMT nanocomposites. The nanocomposites had good processability and lower viscosity than that of SMAH.

关 键 词：SMAH 蒙脱土 纳米复合材料 PA6 

分 类 号：TB332[一般工业技术—材料科学与工程] O632.12[理学—高分子化学]