Si对中碳弹簧钢氧化脱碳行为的影响  

Effect of Si on Behavior of Oxidation and Decarburization of Medium Carbon Spring Steels

作　　者：石如星[1] 姚春发[2] 惠卫军[2] 雍歧龙[2] 聂义宏[2] 项金钟[1] 

机构地区：[1]云南大学物理科学技术学院,昆明650091 [2]先进钢铁材料技术国家工程研究中心,北京100081

出　　处：《特殊钢》2008年第3期19-20,共2页Special Steel

基　　金：973国家重点基础研究发展规划资助项目(2004CB619104)

摘　　要：试验研究了成分(%)为0.49C-0.29Si-1.65Mn、n53C-0.78Si-1.56Mn和0.54C-1.74Si-0.71Mn(60Si2MnA)3种中碳弹簧钢850℃5～120 min水冷和780～1000℃60 min水冷热处理后的脱碳敏感性和氧化失重行为。结果表明,随钢中硅含量增加,钢的脱碳层深度增加,氧化失重量减少,说明Si能增加钢中碳的扩散系数,促进钢的脱碳。The behavior of decarburization sensitivity and oxidation weight loss of three medium carbon spring steels ： 0. 49C-0.29Si-1.65Mn, O. 53C-0. 78Si-1.56Mn and 0. 54C-1.74Si-0. 71Mn （6Si2MnA） heat-treated at 850 ℃ for 5 ～ 120 min, water cooling, and at 780～1 000 ℃ for 60 min water cooling has been tested and studied. Results showed that with increasing silicon content in steel, the decarburization depth increased and the weight loss of oxidation decreased. It indicates that Si can increase coefficient of diffusion of carbon in steel to improve decarburization of steel.

关 键 词：硅 中碳弹簧钢 脱碳 氧化 

分 类 号：TG142.15[一般工业技术—材料科学与工程]