膨润土为原料微波辐射法合成高稳定性介孔分子筛  

Microwave Radiation Synthesis of Mesoporous Molecular Sieve with High Stability Using Natural Clay as Raw Material

作　　者：唐雅静[1] 姜廷顺[1] 张蓉仙[1] 赵谦[1] 殷恒波[1] 

机构地区：[1]江苏大学化学化工学院,镇江212013

出　　处：《纳米技术与精密工程》2008年第3期185-189,共5页Nanotechnology and Precision Engineering

基　　金：镇江市工业攻关项目(GY2006017);江苏大学高级人才基金资助项目(JDG2006074)

摘　　要：在碱性条件下,以硅酸钠、氯化铝和膨润土为原料,十六烷基三甲基溴化铵为模板剂,用微波辐射法合成高稳定性的介孔分子筛.经XRD、FT-IR、氮气物理吸附、差热分析和TEM等手段进行表征,结果表明可合成出高有序性、具有典型六方介孔结构的介孔分子筛.样品经550,℃焙烧3,h后,比表面积为576,m2/g,平均孔径为4.83,nm,经750,℃焙烧3,h或在100,℃下水热处理12,d后仍具有较好的介孔有序性.Mesoporous molecular sieve with high stability was synthesized by microwave radiation method using natural clay, sodium silicate and aluminium chloride as raw materials and cetyl trimethyl ammonium bromide （ CTAB ） as a template agent under alkaline condition.The samples were characterized by means of X-ray diffraction （ XRD ） , Fourier transform-infrared （FT-IR） , N2 physical adsorption, thermal gravimetric-differential scanning calorimeter （TG-DSC） and transmission electron microscopy （ TEM ） , respectively. The results show that the synthesized sample has a typical hex- agonal mesoporous structure with a good mesoporous ordering. On the other hand, the synthesized sample has a surface area of 576 m2/g and an average pore size of 4.83 nm after calcination at 550℃ for 3 h. Furthermore,the sample still has a good mesoporous ordering after calcination at 750 ℃ for 3 h or hydrothermal treatment at 100℃ for 12 d.

关 键 词：膨润土 微波辐射法 介孔分子筛 稳定性 表征 

分 类 号：TQ424.25[化学工程]