Photoluminescence Property of Eu-doped Calcium Aluminium Silicate Glasses  

作　　者：林耿 邱建荣 

机构地区：[1]State Key Laboratory of High Field Laser Physics,Shanghai Institute of Optics and Fine Mechanics,Chinese Academy of Sciences [2]State Key Laboratory of Silicon Materials,Zhejiang University,Hangzhou 310027,China [3]State Key Laboratory of Silicon Materials,Zhejiang University

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2007年第B12期787-789,共3页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the National Natural Science Foundation of China (No.50672087 and No.60778039);National Basic Research Program of China (No.2006CB806000);National High Technology Program of China (No.2006AA03Z304);supported by Program for Changjiang Scholars and Innovative Research Team in University

摘　　要：We report on a simple anti novel method to induce Si-related oxygen-deficient defects in CaO-Al2O3-SiO2 glasses by using Al metal nstead of part Al2O3 Blue emission is observed from the glass samples. Moreover, the quantities of the oxygen-deficient defects can be controlled by adjusting AI content. We also prepare glass samples using AI instead of part Al2O3 and doped with Eu^3＋ ions. Addition of Al results in reduction of Eu^3＋ ions to Eu^2＋ ions and change of the luminescence property. The investigation made on to control and characterize the defects could lead to the development of more efficient economical materials with improved properties.We report on a simple anti novel method to induce Si-related oxygen-deficient defects in CaO-Al2O3-SiO2 glasses by using Al metal nstead of part Al2O3 Blue emission is observed from the glass samples. Moreover, the quantities of the oxygen-deficient defects can be controlled by adjusting AI content. We also prepare glass samples using AI instead of part Al2O3 and doped with Eu^3＋ ions. Addition of Al results in reduction of Eu^3＋ ions to Eu^2＋ ions and change of the luminescence property. The investigation made on to control and characterize the defects could lead to the development of more efficient economical materials with improved properties.

关 键 词：calcium aluminosilicate Si-related defects luminescence properties 

分 类 号：TQ171.7[化学工程—玻璃工业]