膜用聚酯母粒热性能研究  

THERMAL BEHAVIOR OF PET MASTER

作　　者：任夕娟[1] 孟家明 高宏保[1] 殷正权[2] 

机构地区：[1]仪征化纤股份有限公司产品技术开发中心 [2]仪征化纤股份有限公司产品技术开发中心,仪征,211900

出　　处：《合成技术及应用》1997年第2期18-20,4,共4页Synthetic Technology & Application

摘　　要：通过DSC、TG研究了膜用聚酯母粒的热性能，分析了DSC潜回上熔体冷却结晶峰、冷结晶峰等热谱特征与工艺适应性的关系．结果表明，熔作冷却结晶峰宽而矮，峰点温度较低，结晶速度较慢的聚酯母位，其拉膜工艺适应性较强；反之则工艺适应性较差。The thermal properties of PET master were investigated by thermal analysis. The relation between the process suitability and T'. peak、 Tc peak that appeared on DSC were studied. The results indicated that the peak shape was wider and shorter, then the process suitability was stronger. Otherwise, the process suitability was weaker.

关 键 词：热性能 结晶 性能 聚酯薄膜 原料 

分 类 号：TQ323.404[化学工程—合成树脂塑料工业]