硅还原转炉熔渣气化脱磷实验研究  

Experimental Study on Gasification Dephosphorization of Converter Slag With Reduction by Silicon

作　　者：王书桓[1] 吴艳青[1] 刘新生[1] 徐志荣[2] 吕晓芳[3] 

机构地区：[1]河北理工大学冶金与能源学院,河北唐山063009 [2]唐山钢铁集团有限责任公司第一轧钢厂,河北唐山063016 [3]邢台职业技术学院,河北邢台054009

出　　处：《钢铁》2008年第2期31-34,共4页Iron and Steel

基　　金：国家自然科学基金资助项目(50444028)

摘　　要：在1773～1973K温度范围内，满足溅渣护炉的炉渣条件下，在真空碳管电阻炉中对转炉渣进行了硅热还原实验研究。结果表明，在影响还原脱磷的因素中温度的影响最大，FeO含量次之，再次是氮气流量，炉渣碱度影响最小。研究确定了适宜溅渣护炉气化脱磷的最佳条件，还原炉渣气化脱磷率最高可以达到81．23％。From 1 773 K to 1 973 K, the reduction experiments of converter slag simulated for slag splashing by silicon were carried out in a vacuum graphite tube resistance furnace. The result indicates that among the four influencing factors of reducing dephosphorization, temperature is uppermost influencing factors, the content of FeO takes the second place, nitrogen takes the third place, and basicity takes the fourth place. The optimum conditions for gasification dephophorization during slag splashing were determined, the gasification dephophorization rate by reduced slag can reach to 81.23%.

关 键 词：转炉渣 还原脱磷 炉渣碱度 正交实验 

分 类 号：TF713[冶金工程—钢铁冶金]