超音速电弧喷射雾化Ag-Cu合金粉末的快速凝固组织  

Rapid Solidification Structure of Ag-Cu Alloy Powders by Ultrasonic Arc Spray

作　　者：秦国义[1] 蔡宏中[2] 赵怀志[2] 宁远涛[2] 

机构地区：[1]昆明理工大学材料与冶金工程学院 [2]昆明贵金属研究所,云南昆明650106

出　　处：《贵金属》2008年第3期11-16,共6页Precious Metals

基　　金：云南省应用基础研究基金(2003E0082M)

摘　　要：采用超音速电弧喷射雾化制备Ag-28%Cu(质量分数)、Ag-10%Cu、Cu-10%Ag合金粉末;用SEM对合金粉末的凝固组织进行了研究。结果表明,Ag-10%Cu、Cu-10%Ag合金粉末的快速凝固组织为微晶胞离异共晶组织;粉末直径≤50μm时,Ag-28%Cu共晶粉末的快速凝固组织为单相亚稳固溶体;粉末直径>50μm时,Ag-28%Cu共晶粉末的快速凝固组织为芯部含有纳米层片共晶组织的亚稳扩展固溶体。Spherical powders of Ag -28 % Cu （ mass fraction） , Ag - 10% Cu and Cu - 10% Ag alloy were prepared by Ultrasonic Arc Spray Atomization process. The microstructure of the rapid solidified alloy powders were investigated by SEM. The textures of Ag - 10% Cu and Cu - 10% Ag alloy powders showed micro - cell structure. The microstructure of the RS Ag - 28% Cu eutectic powder is the single metastable fcc solid solution when the powder particle size is ≤50μm, and the metastable expanded solid solutions containing micro -eutectic structure with nanometer scales when the powder particle size is 〉 50μm.

关 键 词：金属材料 超音速电弧喷射雾化 快速凝固 AG-CU合金 

分 类 号：TG146.32[一般工业技术—材料科学与工程]