SBS/蒙脱土纳米复合材料的流变行为  

Rheoloigical behavior of SBS/montmorillonite nanocomposites

作　　者：陈中华[1] 冯润财[1] 

机构地区：[1]华南理工大学材料科学与工程学院,广东广州510640

出　　处：《弹性体》2008年第3期28-32,共5页China Elastomerics

摘　　要：用毛细管流变仪测定并研究了热塑性丁苯三嵌段共聚物(SBS)/蒙脱土纳米复合材料的熔体的稳态剪切流变行为,研究结果表明:温度和压力一定的条件下,加入一定量的改性蒙脱土可以降低熔体的粘度;在较低的剪切速率下,即出现剪切变稀现象;在高剪切速率下,粘度对剪切速率的敏感性是降低的,改性蒙脱土加入量对熔体的剪切粘度影响较小,主要是由基体材料所决定的;随温度的升高熔体粘度对剪切速率的敏感性是降低的。采用转矩流变仪对材料的加工性能进行研究,发现复合材料的加工性能基本上保持了纯SBS的加工性能。The steady rheological behavior of melts for nanocomposites composed of poly（styreneb-butadiene-b-styrene） （SBS）and different content of modified montmorillonite （KS120, KS80） was studied. The result revealed that addition of modified montmorillonite can lower the viscosity of melts. At lower shear rate the melts for the nanocomposites exhibited shear-thinning. And the melts flow depended weakly on the shear rate and content of modified montmorillonite, but the SBS matrix at high shear rate. With the temperature increase, viscosity of melts became weakly dependence on shear rate.

关 键 词：SBS 蒙脱土 纳米复合材料 流变行为 

分 类 号：TQ334.3[化学工程—橡胶工业] TQ330.38