Enhanced optical nonlinear absorption of graded Au-TiO_2 composite films  

作　　者：刘莉 苏雄睿 

机构地区：[1]College of Electronics & Information Engineering, Wuhan University of Science and Engineering [2]Department of Physics, Wuhan University

出　　处：《Chinese Physics B》2008年第6期2170-2174,共5页中国物理B（英文版）

基　　金：Project supported by the National Natural Science Foundation of China (Grant No 10474075)

摘　　要：This paper reports that single-layer and graded Au-TiO2 granular composite films with Au atom content 15%- 66% were prepared by using reactive co-sputtering technique. The third-order optical nonlinearity of single-layer and graded composite films was investigated by using s- and p-polarized Z-scans in femtosecond time scale. The nonlinear absorption coefficient βeff of single-layer Au-TiO2 films is measured to be -2.3×10^3-0.76×10^3 cm/GW with Au atom content 15%-66%. The βeff value of the 10-layer Au-TiO2 graded film is enhanced to be -2.1×10^4cm/GW calculated from p-polarized Z-scans, which is about ten times the maximum βeff of single-layer films. Broadened response in the wavelength region 730-860 nm of the enhanced optical nonlinearity of graded Au-TiO2 composite films was also investigated.This paper reports that single-layer and graded Au-TiO2 granular composite films with Au atom content 15%- 66% were prepared by using reactive co-sputtering technique. The third-order optical nonlinearity of single-layer and graded composite films was investigated by using s- and p-polarized Z-scans in femtosecond time scale. The nonlinear absorption coefficient βeff of single-layer Au-TiO2 films is measured to be -2.3×10^3-0.76×10^3 cm/GW with Au atom content 15%-66%. The βeff value of the 10-layer Au-TiO2 graded film is enhanced to be -2.1×10^4cm/GW calculated from p-polarized Z-scans, which is about ten times the maximum βeff of single-layer films. Broadened response in the wavelength region 730-860 nm of the enhanced optical nonlinearity of graded Au-TiO2 composite films was also investigated.

关 键 词：Au-TiO2 granular composites graded composite films Z-SCAN optical nonlinear absorption 

分 类 号：O484.41[理学—固体物理]